Abstract
Zeolitic imidazolate framework-67 (ZIF67) has been regarded as an effective energy storage material due to its high surface area and electroactive cobalt center. Carbonizing ZIF67 can enhance electrical conductivity by converting 2-methylimidazole (2-melm) to carbon with cobalt doping. In this work, a novel in situ electrospinning is proposed to fabricate carbonized ZIF67 on carbon fiber (C67@PAN-OC) as a freestanding supercapacitor electrode. Polyacrylonitrile solution containing a cobalt precursor is used for electrospinning, and produced fibers are immersed in 2-melm to form ZIF67. Individually grown carbonized ZIF67 on carbon fiber is obtained using the in situ electrospinning method, while the one-body mixed carbon electrode is formed using the ex situ electrospinning method. A highest specific capacitance (CF) of 386.3 F/g at 20 mV/s is obtained for the in situ synthesized C67@PAN-OC electrode due to the largest electrochemical surface area and the smallest resistance, while the ex situ synthesized electrode only shows a CF value of 27.7 F/g. A symmetric supercapacitor (SSC) assembled using the optimized C67@PAN-OC electrodes and gel electrolytes shows a maximum energy density of 9.64 kWh/kg at 0.55 kW/kg and a CF retention of 59.5% after 1000 times charge/discharge process. A CF retention of 75.6% after bending 100 times is also obtained for SSC.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.