Abstract
Nitrogenated ultrananocrystalline diamond/hydrogenated amorphous carbon composite films were prepared in a hydrogen and nitrogen mixed-gas atmosphere by pulsed laser deposition with graphite targets. The electrical conductivity in n-type conduction remarkably increases to 18 §Ù–1×cm–1 at 300 K with an increase in the nitrogen content up to 7.9 at.%. In the nitrogen content range from 7.9 to 10.4 at.%, the electrical conductivity is suddenly and dramatically decreased down to 0.03 §Ù–1·cm–1 in reverse, accompanied by the disappearance of diamond grains in the films. A huge number of grain boundaries owing to the existence of diamond grains embedded in UNCD/a-C:H films, which is structural specific to UNCD/a-C:H, should play a significant role in the large electrical conductivity enhancement by nitrogen doping. The X-ray photoemission and near-edge X-ray fine-absorption spectroscopic measurements could not detect an evident difference in the spectra that explain the sudden irregular change in the electrical conductivity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.