Abstract
Photo-enhanced chemical (PEC) wet etching technology was used to etch GaN and AlGaN epitaxial layers. It was found that the maximum etch rates were 510, 1960, 300, and 0 nm/mm for GaN, Al 0.175Ga 0.825N, Al 0.23Ga 0.77N, and Al 0.4Ga 0.6N, respectively. It was also found that we could achieve a high Al 0.175Ga 0.825N to GaN etch rate ratio of 12.6. Nitride-based Schottky diodes and heterostructure field effect transistors (HFETs) were also fabricated by PEC wet etching. It was found that we could achieve a saturated I D larger than 850 mA/mm and a maximum g m about 163 mS/mm from PEC wet etched HFET with a 0.5 μm gate length. Compared with dry etched devices, the leakage currents observed from the PEC wet etched devices were also found to be smaller.