Abstract
In this work, electro-less plating was adopted to produce a new metallic bipolar plate coated with amorphous alloy. The Ni-P amorphous alloy thin film was deposited on Al plate with a bipolar plate flow field and its corrosion resistance and contact electrical resistance were measured. As results, it was found that the electro-less plated Ni-P amorphous thin film showed much lower corrosion resistance than the Ni-CrP-B metallic glass because of its lack of Cr content and also found that the Ni-P film showed lower contact electrical resistance than the stainless steel SUS316L plate. The electricity generation tests with the single cell having the Ni-P amorphous alloy-coated bipolar plates produced in this study revealed that the single cell with the Ni-P amorphous alloy-coated bipolar plates showed excellent I-V performance as well as the cell with the carbon bipolar plates after 39th repetition. However, the I-V performance degraded gradually and was found to be much lower than that with the carbon bipolar plates after 50th repetition. Then the long time durability tests for 24 h were also conducted at the constant current density of 200 mAcm 2 . It was found that the cell voltage of the single cell with the Ni-P amorphous alloy-coated bipolar plates decreased gradually
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.