Abstract
Previously unreported σ-phases in the ternary niobium-based systems Nb-X-Ga for X = Ru, Rh, Pd, Ir, Pt, Au, and Nb-X-Al for X = Ir, and Pt are presented, prepared by arc-melting followed by annealing at 1000 °C for 1 week. The phases are primitive tetragonal (P42/mnm, no. 136) with lattice parameters of a = 9.8336(2)-9.9432(1) Å and c = 5.1098(1)-5.1718(1) Å. Refinements of the single crystal X-ray diffraction data for the Ru and Ir containing materials gave the formulas Nb20Ru5Ga5 and Nb20Ir4Ga6, showing mixing of X/Ga on the crystallographic 8i2 and 2a sites of the structure, a type of disorder frequently found in σ-phases. We present a graphical classification for ternary σ-phases that places our materials in context with previous materials. The materials do not show evidence of bulk superconductivity above 2 K. Synthesis of equivalent Ta-based σ-phases was attempted but they were not found.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.