Neutron irradiation effects on magnetic minor hysteresis loops in nuclear reactor pressure vessel steels

Abstract

Magnetic minor hysteresis loops have been measured on A533B-type nuclear reactor pressure vessel steels with various combinations of Cu and Ni contents after neutron irradiation to a fluence up to 3.32 × 1019 n cm−2. A strong compositional dependence of minor-loop properties, which are indicators of internal stress, was found. The properties of high-Cu and high-Ni steel show a large increase in the low fluence regime below 0.4 × 1019 n cm−2, followed by a slow decrease, while those for low-Cu or low-Ni steel show a sudden decrease. The changes are roughly in linear proportion to the yield strength changes. The results were explained from the viewpoint of the formation and growth of Cu-rich precipitates and/or fine scale defects in the matrix and along pre-existing dislocations.