Abstract
Liquid metal embrittlement (LME) of a Fe-10Cr-4Al ferritic steel was studied at 375 °C in liquid Pb-Bi alloys. Slow strain rate testing (SSRT) in low oxygen conditions was used to evaluate the ductility as a function of Bi concentration. It was found that susceptibility to LME increased strongly with the Bi concentration. The steel showed a reduction in its total strain to failure, which started at 3–5 wt.% Bi. The alloying elements (Fe, Cr, and Al) have a higher solubility in Bi than pure lead (Pb), so they are expected to dissolve more readily when Bi is added to the Pb. This is believed to be part of the explanation for the observed increase of LME. Lead with up to 3 wt.% Bi induced no LME in the studied corrosion resistance FeCrAl alloy.