Near-unity blue-orange dual-emitting Mn-doped perovskite nanocrystals with metal alloying for efficient white light-emitting diodes

Abstract

The tunable dual-color emitting Mn2+ doped CsPbCl3-xBrx nanocrystals (NCs) with near-unity photoluminescence quantum yield (PL QY) were synthesized through post-treatment of metal bromide at room temperature for fabrication of efficient warm white light-emitting diodes (WLEDs). Especially, the CdBr2 treated blue-orange emitting Mn doped NCs with various Mn/Pb molar feed ratios exhibit higher PL QY of 97% and longer Mn2+ PL lifetime of 0.9 ms. It is surprisingly found that the X-ray diffraction peak at 31.9° is almost not changed with increasing Br composition, meaning formation of metal alloying due to incorporation of amount of divalent cation in NCs. The strong and stable Mn2+ PL at temperature ranging from 80 K to 360 K are revealed and the temperature-dependent energy transfer efficiencies in Mn2+ doped CsPbCl1.5Br1.5 NCs are obtained. The enhancement mechanism of Mn2+ PL QY was attributed to improved energy transfer from exciton to Mn2+ d–d transition and suppressed defect state density after post-treatment. The efficient warm WLEDs with color rendering index of 90 and luminous efficacy of 92 lm/W at 10 mA were fabricated by combining blue-orange dual-emitting Mn2+ doped CsPbCl3-xBrx@SiO2 and green emissive CsPbBr3@SiO2 NCs with violet GaN chips.