Abstract
A thin industrial corrosion-protection nanostructured coating for the Al alloy AA2024-T3 is demonstrated. The coating is prepared in a two-step process utilizing hard anodizing as a pre-treatment, followed by sealing and coating by atomic layer deposition (ALD). In the first step, anodizing in sulfuric acid at a low temperature converts the alloy surface into a low-porosity anodic oxide. In the second step, the pores are sealed and coated by low-temperature ALD using different metal oxides. The resulting nanostructured ceramic coatings are thoroughly characterized by cross-sectioning using a focused ion beam, followed by scanning electron microscopy, transmission electron microscopy, X-ray microanalysis, and nanoindentation and are tested via linear sweep voltammetry, electrochemical impedance spectroscopy, salt spray, and energetic atomic oxygen flow. The best thin corrosion protection coating, made by anodizing at 20 V, 1 °C and sealing and coating with amorphous Al2O3/TiO2 nanolaminate, exhibits no signs of corrosion after a 1000 h ISO 9227 salt spray test and demonstrates a maximum surface hardness of 5.5 GPa. The same coating also suffers negligible damage in an atomic oxygen test, which is comparable to 1 year of exposure to space in low Earth orbit.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.