Abstract
GdBa2Cu3O7-x coated conductors were splice jointed by a face-to-face manner using a paste containing nano-sized Ag particles under a pressure of about 50 MPa at 150 °C for 1 hr. The low electrical resistance of 6 nΩ at the joint was attained. Nanostructural characterizations of the starting Ag paste and the jointed region of the coated conductors were carried out using scanning electron microscopy and transmission electron microscopy. The size of the Ag particles in the starting pastes were confirmed to be a few tens of nanometers in diameter. The size of Ag particles became larger during the jointing process. Both the surfaces of the stabilizing Ag layers were partially bonded by the Ag particles. No oxides or other elements were detected in the region of the bonding parts.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.