Abstract
Ti–B–N films with a gradient in the chemical composition were deposited onto austenitic stainless steel sheets by means of unbalanced DC magnetron co-sputtering using a segmented TiN\\Tib2 target. Film microstructure was characterized by means of electron-probe microanalysis (EPMA), transmission electron microscopy (TEM), electron energy-loss spectroscopy (EELS), and X-ray diffraction (XRD) as well as glancing angle X-ray diffraction (GAXRD). The mechanical properties of the coatings were measured using a depth-sensing nanoindenter. The composition of the films was found to lie close to the quasi-binary section TiN–TiB2 within the ternary system Ti–B–N. The grain size determined from TEM investigations range between 3 and 5 nm. Coatings consisted of a nanocrystalline fcc TiN phase (with boron atoms and oxygen impurities dissolved), and TiB2, TiB and B2O3. Microstructure as well as chemical composition of the films were not influenced significantly by the deposition parameters used in this investigation. Contrary, the mechanical properties were strongly influenced varying the ion bombardment. Hardness values exceeding 50 GPa and elastic moduli close to 500 GPa were obtained.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.