Abstract
The soft magnetic properties of the nanocrystalline Fe–M–B (M=Zr,Nb) alloys, which exhibit a high saturation flux density (Bs) above 1.5 T as well as a high effective permeability (μe) above 30 000 at 1 kHz, were found to be improved by adding small amounts of Cu and by optimizing the chemical composition. The addition of Cu to the alloys decreases the bcc grain size. The excellent soft magnetic properties (a high μe of 100 000 at 1 kHz combined with a high Bs of 1.53 T) can be achieved in the region where small grain size, as well as nearly zero-magnetostriction are obtained, which is attained in the compositional range around Fe84Nb3.5Zr3.5B8Cu1. The soft magnetic properties can be further improved by low temperature annealing before the crystallization treatment, probably as a result of a decreased grain size distribution in the crystallized state. Consequently, the μe reaches the maximum value of 120 000 for the nanocrystalline Fe84Nb3.5Zr3.5B8Cu1 alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.