Nanocomposites of ultrahigh molar mass polyethylene and modified carbon nanotubes

Abstract

ABSTRACTIn this work, the use of a laboratory twin‐screw extruder was evaluated to process ultrahigh molar mass polyethylene and composites with carbon nanotubes (CNTs). Commercial polymer samples with lubricant (1%) and different percentages (0.01%, 0.05%, and 0.1%) of pure, oxidized, and chemically surface treated multi‐walled carbon nanotubes (MWCNTs) were evaluated. The results showed that polymer melting and crystallization temperatures were not affected by CNTs, although an increase in the degree of crystallinity in all nanocomposites was observed along with a decrease in crystal size. Therefore, CNTs behaved as nucleating agents. All ultrahigh molar mass polyethylene (UHMWPE)/CNT samples showed increased initial degradation temperature, although this was not very great when introducing acetylated and stearic acid modified CNTs. Both oxidized CNTs and stearic acid CNTs did not markedly improve the composites' mechanical properties. Therefore, the nanocomposites containing pure CNTs and most of those with acetylated CNTs resulted in higher reinforcement for UHMWPE. The addition of the lubricant allowed the polymer matrix to be processed in the extruder, whereas the increase in CNT content in UHMWPE improved the stiffness of the material. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019, 136, 47459