Abstract
Grain boundary wetting as a preliminary stage for zinc-induced grain boundary weakening and embrittlement in a Zn-coated press-hardened 20MnB8 steel was analyzed using electron backscatter diffraction, Auger electron spectroscopy, energy dispersive X-ray analysis, atom probe tomography and transmission electron microscopy. Microcracks at prior austenite grain boundaries were observed. Structures that developed after microcrack formation were identified: for example, Zn/Fe intermetallic phases with grain sizes smaller than 100 nm were present at the crack surfaces and the wedge-shaped crack tips. An electrolytically coated reference sample that underwent the same heat treatment as the press-hardened material but without the application of tensile stress was investigated in order to find the initial cause of the microcracks. On this sample, Zn, in the order of one atomic layer, was found along prior austenite grain boundaries several micrometers away from the actual Zn/Fe phases in the coating. The resulting grain boundary weakening with the Zn wetting of prior austenitic grain boundaries during austenitization and/or hot forming is a necessary precondition for microcrack formation.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call