Abstract
AbstractWe report the metal organic vapor phase epitaxy (MOVPE) growth and characterization of non‐polar (11$ \bar 2 $0) a ‐plane Alx Ga1–xN on (1$ \bar 1 $02) r ‐plane sapphire substrates over the entire composition range. Alx Ga1–xN samples with ∼0.8 μm thick layers and with x = 0, 0.18, 0.38, 0.46, 0.66, and 1.0 have been grown on r ‐plane sapphire substrates. The layer quality can be improved by using a 3‐stage AlN nucleation layer and appropriate V/III ratio switching following nucleation. All a ‐plane AlGaN epilayers show an anisotropic in‐plane mosaicity, strongly influenced by Al incorporation and growth conditions. Careful lattice parameter measurements show anisotropic in‐plane strain that results in an orthorhombic distortion of the hexagonal unit cell, making Al composition determination from X‐ray diffraction difficult. In general lower Al incorporation is seen in a ‐plane epilayers compared to c ‐plane samples grown under the same conditions. (© 2010 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: physica status solidi (RRL) – Rapid Research Letters
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.