Abstract
Various oxide powders were prepared by the emulsion combustion method (ECM) using metal precursors, kerosene, and a surfactant. The product particles were characterized by transmission electron microscopy (TEM), nitrogen adsorption, and X‐ray diffraction. Hollow γ‐Al2O3 particles were produced from aluminum nitrate or chloride precursors dispersed in air, whereas dispersion of the precursor emulsion in oxygen resulted in solid α‐Al2O3 particles. Hollow spheres were obtained also for TiO2, ZrO2, and Y2O3 by ECM of TiCl4, zirconium oxynitrate, and yttrium nitrate in aqueous solution. A simple method was developed to predict the thickness and diameter of hollow particles using the nitrogen adsorption data and initial droplet concentration of the ECM spray. The TEM diameter and shell thickness of hollow particles were consistent with those predicted. In contrast, solid particles were formed by ECM for ZnO, Fe2O3, CeO2, and MgO from aqueous solutions of their corresponding nitrates.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.