Abstract
Electrical properties of poly(e-caprolactone) (PCL)/poly(vinyl butyral) (PVB) blends containing carbon black (CB) were studied as a function of a small amount of PVB content and a wide range of molecular weight of PVB. For samples with the same CB content, the intensity of positive temperature coefficient (I PTC , defined as the ratio of peak resistivity to resistivity at room temperature) of the blends was increased, with PVB content greatly and molecular weight of PVB weakly. As the band spacings of PCL spherulites in PCL/PVB blends decrease with PVB content and molecular weight of PVB, the changes of the positive temperature coefficient property are ascribed to the morphological difference (i.e., period of twisted lamellae) in the blends. We confirmed our previous conclusion that the origin of the positive temperature coefficient phenomenon is the changes of the distribution of the CB on the melting of the crystalline phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.