Abstract
AbstractThree kinds of micron‐sized monodispersed polystyrene (PS)/ poly(styrene ‐ divinylbenzene) composite particles were produced by two kinds of seeded copolymerizations of styrene (S) and divinylbenzene (DVB) (PS seed/ (S+DVB)=2/1, wt. ratio; S/DVB=1/1, molar ratio) in the presence of about 2 μm‐sized monodispersed PS particles, and their morphologies were examined. One was produced by a seeded dispersion copolymerization where almost monomers and initiators exist in an ethanol/water (12.6/4.0, w/w) medium. The others two were produced by seeded copolymerizations with the dynamic swelling method where almost monomers exist in the monomer‐swollen particles using 2, 2'‐azobisisobutyronitrile in monomer‐swollen PS seed particles or using 4, 4'‐azobis (4‐cyanopentanoic acid) in an ethanol/water (7/43, w/w) medium. In the former polymerization, the produced composite particles had a high dense crosslinked shell, whereas in the latter two polymerizations, they did the comparatively homogeneous crosslinked structures.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.