Abstract
AbstractTemperature-dependent small-angle X-ray scattering spectroscopy of isothermally cold crystallized isotactic polystyrene revealed considerable morphological reorganization during subsequent heating to the melt. Both the crystalline thickness and the long period increased continuously with increasing temperature before the samples finally melted. The temperature dependence of these changes correlated very well with the melting behaviour observed with differential scanning calorimetry. As the temperature increased during a heating scan, the initial lamellae that formed during isothermal crystallization showed only little reorganization until they started to melt. Then, the molten material recrystallized continuously into increasingly thicker lamellae at increasing temperature until they finally melted. As the crystallization temperature approached the final melting temperature of the recrystallized lamellae, the initial lamellae melted without further recrystallization and no morphological changes were seen in this case.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.