Abstract
GaAs 1−x Bi x epilayers with bismuth concentrations up to x=3.1% were grown on GaAs by molecular beam epitaxy. The Bi content in the films was measured by Rutherford backscattering spectroscopy. X-ray diffraction shows that GaAsBi is pseudomorphically strained to GaAs but that some structural disorder is present in the thick films. The extrapolation of the lattice constant of GaAsBi to the hypothetical zincblende GaBi alloy gives 6.33±0.06 Å. Room-temperature photoluminescence of the GaAsBi epilayers is obtained and a significant redshift in the emission of GaAsBi of ∼84 meV per percent Bi is observed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.