Modulation of Vacancy Defects and Texture for High Performance n-Type Bi2 Te3 via High Energy Refinement.

Abstract

The carrier concentration in n-type layered Bi2 Te3 -based thermoelectric (TE) material is significantly impacted by the donor-like effect, which would be further intensified by the nonbasal slip during grain refinement of crushing, milling, and deformation, inducing a big challenge to improve its TE performance and mechanical property simultaneously. In this work, high-energy refinement and hot-pressing are used to stabilize the carrier concentration due to the facilitated recovery of cation and anion vacancies. Based on this, combined with SbI3 doping and hot deformation, the optimized carrier concentration and high texture degree are simultaneously realized. As a result, a peak figure of merit (zT) of 1.14 at 323 K for Bi2 Te2.7 Se0.3 + 0.05 wt.% SbI3 sample with the high bending strength of 100 Mpa is obtained. Furthermore, a 31-couple thermoelectric cooling device consisted of n-type Bi2 Te2.7 Se0.3 + 0.05 wt.% SbI3 and commercial p-type Bi0.5 Sb1.5 Te3 legs is fabricated, which generates the large maximum temperature difference (ΔTmax ) of 85 K at a hot-side temperature of 343 K. Thus, the discovery of recovery effect in high energy refinement and hot-pressing has significant implications for improving TE performance and mechanical strength of n-type Bi2 Te3 , thereby promoting its applications in harsh conditions.