Abstract
This article investigates the influence of temperature and strain on second‐phase transformation strengthening and the resulting mechanical properties in a lean AISI 301LN austenitic stainless steel within a temperature range of −60 to 180 °C. The volume fraction of martensite evolved is determined using nondestructive magnetic Ferritescope measurements that are adjusted by using a calibration factor of 1.7, which is established using the saturation magnetization measurements, X‐ray, and neutron diffraction measurements. The kinetics of strain‐induced martensite transformation (SIMT) as a function of strain and temperature is accurately described by a set of modified constitutive Boltzmann sigmoidal equations at temperatures below 75 °C. For this steel, the Md (30/50) temperature is determined as 61 °C. The absolute Md temperature is established as ≈109 °C, and no athermal transformation to martensite is observed upon cooling to −270 °C using cryogenic neutron diffraction facilities. Extended JMAK analysis of the transformation is used to shed light on the mechanism of martensitic transformation. It is found that the transformation‐induced plasticity (TRIP) effect due to SIMT is at a maximum at 75 °C, which is the maximum elongation temperature (MET) and calculations are performed regarding alloy development which will reduce the MET to room temperature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.