Abstract
It is generally recognized that high-temperature treatments, namely annealing, influence the microstructure and the morphology, which, in turn, determine the mechanical properties of polymeric parts. Therefore, annealing can be adopted to control the mechanical performance of the molded parts. This work aims to assess the effect of annealing on the morphology developed in isotactic polypropylene (iPP) injection-molded parts. In particular, a two-step annealing is adopted: the polymer is injected in a mold at a high temperature (413 or 433 K), which is kept for 5 min (first annealing step); afterward, the mold temperature is cooled down at 403 K and held at that temperature for a time compatible with the crystallization half-time at that temperature (second annealing step). The characterization of morphology is carried out by optical and electronic scanning microscopy. The temperature of the first annealing step does not influence the thickness of the fibrillar skin layer; however, such a layer is thinner than that found in the molded parts obtained without any annealing steps. The second annealing step does not influence the thickness of the fibrillar skin layer. The dimension of spherulites found in the core is strongly influenced by both annealing steps: the spherulite dimensions enlarge by the effect of annealing steps. A model that considers spherulite and fibril evolutions is adopted to describe the effect of molding conditions on the final morphology distribution along the part thickness. The model, which adopts as input the thermo-mechanical histories calculated by commercial software for injection molding simulation, consistently predicts the main effects of the molding conditions on the morphology distributions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.