Abstract
The critical current density (Jc) of YBa2Cu3Oy (YBCO)-coated conductors in a magnetic field can be enhanced by the doping of flux-pinning centers in a metal organic deposition (MOD) process with trifluoroacetates (TFA). The size of these flux-pinning centers should be less than 10 nm to achieve commercial use due to the coherence length of YBCO at 77 K. In this paper, BaHfO3 (BHO) nanoparticles were introduced into YBCO films using the TFA-MOD method. Microstructures and the Jc properties of the films prepared using a two-step heating process at crystallization were compared with film prepared using a conventional one-step heating process. The two-step heating process produced 15 nm average-sized BHO nanoparticles in the film compared to 19 nm nanoparticles in a film prepared using a one-step process. It was revealed that the size of nanoparticles in the films could be miniaturized by improving the heating processes in the MOD method, and the miniaturized nanoparticles could contribute to increased Jc in magnetic fields. The mechanism of miniaturization is also discussed based on microstructure observations of quenched films.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.