Abstract
Synthesis of mechanically stable porous scaffolds with an architecture analogous to cancellous bone tissue poses significant challenges to bioactive glass (BG) based scaffolds. This is primarily due to densification and crystallization of the BG's during heat treatment. This study presents a modified BG series (42SiO2-xTiO2-24Na2O-21CaO-13P2O5, where x = 8 and 16 TiO2). TiO2 replaced the SiO2 concentration in the glass and was incorporated due to its biocompatibility and influence on glass structure. Material characterization determined that TiO2 did not induce crystallization within the glass but did increase the glass transition temperature (Tg) from 520°C to 600°C thereby indicating a more stable network connectivity. Scaffolds were synthesized using the foam replication method, resulting in scaffolds with a pore size of approximately 500 μm with the BG-4 composition (30SiO2-12TiO2-24Na2O-21CaO-13P2O5) retaining its amorphous character post-heat treatment. Scaffold ion release was monitored over 5-60 days in simulated body fluid (SBF). Si4+ release was found to decrease, while Ca2+ levels increased in SBF as TiO2 replaced SiO2 within the glass series. Cytocompatibility studies revealed that MC3T3 Osteoblast cells proliferated on the BG-4 scaffold surface and at its interface within culture media, and cell numbers were not significantly reduced.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of biomedical materials research. Part B, Applied biomaterials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.