Abstract
Monophase calcium zirconate (CaZrO3) has been prepared from the equimolar ZrO2 + CaCO3 mixture by two-step synthesis process. In the first step, mechanical treatment of the mixture is performed in an AGO-2 planetary ball mill. In the second step, the milled mixture is annealed to form calcium zirconate. High-energy ball milling of the (ZrO2+CaCO3) mixture results in decrease in the temperature of CaZrO3 formation during annealing at 950 °C. The enhancement of CaZrO3 synthesis is due to accumulation of excess energy by the reagents, decreasing the particle size and notable increase in the interphase area because of “smearing” of CaCO3 on ZrO2 particles during milling. Nanocrystalline calcium zirconate has been produced by controlling the annealing temperature and time.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.