Abstract
A one-step microwave-assisted polyol method was used to fabricate FexZn1−xO (x = 0.01, 0.05, 0.10) nanoparticles. Zinc acetate dihydrate, iron (III) acetylacetonate, oleic acid and diethylene glycol were placed in a Teflon-lined reaction vessel. The reaction mixture was heated up to 250 °C for 15 min in a microwave reactor. The surface modification with oleic acid prevented agglomeration of the nanoparticles. The X-ray diffraction analysis revealed characteristics wurtzite hexagonal structure of ZnO and successful incorporation of the Fe dopant into the host crystal lattice. Doping of ZnO by Fe led to bandgap modification as estimated by Tauc plot. The as-prepared nanopowders were dispersed in toluene and mixed with a poly[2-methoxy-5-(2-ethylhexyloxy)-1,4-phenylenevinylene] (MEH-PPV) polymer to make stable homogenous dispersions. Then, the FexZn1−xO/MEH-PPV nanocomposite thin films were prepared by spin coating and used as thin active layers in polymer light-emitting diodes. The thickness of deposited FexZn1−xO/MEH-PPV film was ca. 30 nm and that of reference neat MEH-PPV film was ca. 25 nm. The electroluminescent spectroscopy study showed that direct blending of MEH-PPV with Fe-doped ZnO nanoparticles is a simple and effective approach to significantly increase the luminance intensity of the diode in comparison to the diode fabricated by neat MEH-PPV.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.