Abstract
AbstractCaBi2Nb2O9 (CBN) ceramic is a promising sensing element to convert vibration to electrical signal at temperatures higher than 600°C. However, conventionally sintered ceramics suffer from poor piezoelectric coefficient (d33) and low electrical resistivity (ρdc). Here, we report that CBN ceramics can be prepared by microwave sintering (MS) to mitigate volatilization issue of Bi2O3 and thus suppress the generation of oxygen vacancies usually seen in conventional sintering (CS) as demonstrated by X‐ray photoelectron spectroscopy (XPS) analysis and mass‐loss measurement. As compared to the CS, the MS is more favorable for reducing the sintering time, and obtaining a dense, fine, and uniform grain morphology as revealed by scanning electron microscopy (SEM) characterizations of both surface and interior of the CBN ceramics, leading to an enhancement of 86% and 75% in d33 and ρdc, respectively. Piezoresponse force microscopy (PFM) as combined with Rayleigh law analysis clearly revealed that the enhancement of piezoelectric properties was attributed to the thinner domains, the higher domain wall density, and the enhanced domain wall motion in the MS‐940 samples. This study paves an important road to simultaneously improve both d33 and ρdc in CBN ceramics for developing high‐temperature vibration sensors.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.