Abstract
ABSTRACTThe goal of this study is to compare thermal and mechanical properties of an epoxy resin system reinforced with SiC nanoparticles using both conventional thermal curing and microwave irradiation techniques. The microwave curing technique has shown potential benefits in processing polymeric nanocomposites by reducing the curing time without compromising the thermo‐mechanical performances of the materials. It was observed from this investigation that, the curing time was drastically reduced to ∼30 min for microwave curing instead of 12 h room temperature curing with additional 6 h post curing at 75°C. Ductile behavior was more pronounced for microwave curing technique while thermal curing showed brittle like behavior as revealed from flexural test. The maximum strain to failure was increased by 25–40% for microwave‐cured nanocomposites over the room temperature cured nanocomposites for the same loading of nanofillers. The glass transition temperature (Tg) also increased by ∼14°C while curing under microwave irradiation. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015, 132, 41708.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.