MICROSTRUCTURES OF ISF SINTERS IN AIR

Abstract

The microstructures of industrial ISF and synthetic sinters were examined. The principle phases present were found to consist of zincite, spinel and glass. The morphologies of the zincite phase in these complex multiphase materials were shown to relate directly to the bulk chemical compositions and thermal histories of the sinters. The conditions favouring the formation of plate-like zincite, essential for the development of refractory networks in the ISF sinters, were identified. The proportion of framework zincite present in the sinters was found to increase with increasing peak bed temperature and an increasing CaO/SiO2 ratio. The aspect ratio of the zincite increases by increasing iron in the solid solution in zincite.On a examiné la microstructure d’agglomérés industriels d’ISF et d’agglomérés synthétiques. On a trouvé que les principales phases présentes consistaient en zincite, en spinelle et en verre. On a montré que la morphologie de la phase de zincite dans ces matériaux complexes à phases multiples était directement reliée à la composition chimique en vrac et au passé thermique des agglomérés. On a identifié les conditions favorisant la formation de zincite lamellaire, essentielle au développement de réseaux réfractaires dans les agglomérés d’ISF. On a trouvé que la proportion de zincite en charpente présente dans les agglomérés augmentait avec l’augmentation du pic de température du lit et avec une augmentation du rapport CaO/SiO2. Le rapport de forme de la zincite augmente par l’augmentation du fer dans la solution solide de la zincite.