Abstract
The amorphous/nanocrystalline duplex structure is stable and exhibits excellent soft magnetic properties. However, the presence of impurities inevitably impacts the performance of the products. In this work, the impact of refining slags with various basicities (R=1, 0.66, 0.5, 0.4) on the microstructure, thermal stability, and soft magnetic properties of Fe81B10P8Cu1 alloy was investigated by varying the composition ratio x:1:1 (x = 2, 3, 4, & 5) of B2O3:MnO:MgO. The utilization of refining slag with low basicity is beneficial for removing impurity, enhancing magnetic exchange interactions and reducing magnetic anisotropy in amorphous alloy, thereby improving its soft magnetic properties. Notably, when the refining slag composition of B2O3:MnO:MgO is 4:1:1, the Fe81B10P8Cu1 nanocrystalline alloy exhibits exceptional soft magnetic properties and the smallest grain size, with a Bs of 1.717 T, Hc of 3.85 A/m and an average grain size of 23.84 nm. These findings are significant for enhancing the performance of Fe-based nanocrystalline alloys.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.