Abstract
A novel Mg alloys of Mg–xZn–ySb (x = 0, 2, 4, 6; y = 0, 0.2, 0.5, 0.8, 1.2) were designed and their microstructure, thermal conductivity and mechanical properties were systematically investigated in the present study. The as-cast Mg–Zn–Sb ternary alloys consist of α-Mg, Mg4Zn7 and Mg3Sb2 phases. Sb addition can refine the eutectic structure (α-Mg + Mg4Zn7) by the growth of Mg4Zn7 on Mg3Sb2 phases. The thermal conductivity of Mg–Zn–Sb alloys decreased with increasing Sb content. There existed an interactive effect of Zn/Sb on the thermal conductivity of the Mg–Zn–Sb alloys. The negative effect of Sb addition on thermal conductivity of alloys was getting smaller with increasing Zn content in alloys. The negative effect of Mg3Sb2 phases on the thermal conductivity of alloys could be weakened by the formation of weak-scattering Mg4Zn7 coated on Mg3Sb2 phases. The best refinement effect on microstructure could be obtained with 0.8 wt%Sb addition. Mg–4Zn–0.8Sb alloy possess the best comprehensive properties with thermal conductivity of over than 120 W/(m·K) and UTS of 185.6 MPa.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.