Abstract
The near-eutectic Sn-3.5 wt.% Ag-0.7 wt.% Cu (Sn-3.5Ag-0.7Cu) alloy was doped with rare earth (RE) elements of primarily Ce and La of 0.05–0.25 wt.% to form Sn-3.5Ag-0.7Cu-xRE solder alloys. The aim of this research was to investigate the effect of the addition of RE elements on the microstructure and solderability of this alloy. Sn-3.5Ag-0.7Cu-xRE solders were soldered on copper coupons. The thickness of the intermetallic layer (IML) formed between the solder and Cu substrate just after soldering, as well as after thermal aging at 170°C up to 1000 h, was investigated. It was found that, due to the addition of the RE elements, the size of the Sn grains was reduced. In particular, the addition of 0.1wt.%RE to the Sn-3.5Ag-0.7Cu solder improved the wetting behavior. Besides, the IML growth during thermal aging was inhibited.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.