Microstructure of titanium deformed by warm extrusion with forward- backward rotating die

Abstract

The principal KoBo device is a press with a forward-backward rotating die, enabling the extrusion of ingots under conditions of constant destabilization of their substructure. Polycrystalline grade 2 titanium was subjected to warm KoBo type extrusion. Microstructure of the material was investigated by means of Electron Backscatter Diffraction (EBSD) in the scanning electron microscope. It clearly shows deformation-induced grain fragmentation. The EBSD maps reveal heterogeneous microstructure built of ribbons curled about the extrusion direction (ED) and some equiaxed or cigar-like grains. Sizes of grains vary in the range 70 – 1500 nm for the minor axis and 350 – 20000 nm for the major axis. The material has a relatively sharp nearly axial texture with the <0001> axis perpendicular to ED. In misorientation angle distribution, besides the peak at low angle boundaries, there are three other peaks at about: 29.7deg, 89.7deg and 93.2deg. They do not correspond to any twin boundaries or low Σ coincidence site lattice misorientations.