Microstructure of diffusion-brazing repaired IN738LC superalloy with uneven surface defect gap width

Abstract

ABSTRACTSlots with uneven width were cut by femtosecond laser in small plates of IN738LC superalloy to imitate service cracks. The ‘cracks’ were repaired by diffusion brazing using BNi-1a or a mixed filler alloy at 1100°C. The joint region was composed of isothermal solidification zone (ISZ), diffusion affected zone (DAZ) and precipitate zone (PZ). The compositions were different between the upper and lower ISZ due to the variation of gap width. The sample, repaired with two kinds of filler metals, had similar DAZ microstructure. PZ of mixed filler alloy bonded sample had a similar microstructure with that of BNi-1a, but less borides. The maximum gap sizes of complete isothermal solidification were almost the same for different filler alloys, followed a square root relationship with time. However, PZ of BNi-1a bonded was larger, resulting from a more base metal dissolution. The relationship between the PZ, ISZ and crack width is discussed.