Microstructure, mechanical properties and superplasticity of the Al–Cu–Y–Zr alloy

Abstract

The phase composition, mechanical properties, and superplastic deformation behavior of a novel Al-4.7Cu-1.6Y-0.3Zr alloy were analyzed. The precipitation of Al3(Zr,Y) dispersoids was observed during a homogenization treatment. The precipitates have an L12 structure and a mean size of 17 and 19 nm at 540 and 590 °C, respectively. The sheets exhibit a yield strength of 292 MPa, an ultimate tensile strength of 320 MPa, and an elongation of 5.3% after simple thermomechanical treatment and annealing at 100 °C. The Al-4.7Cu-1.6Y-0.3Zr alloy exhibits superplasticity with m > 0.4 and elongation of 300–400% within a temperature range of 550–580 °C and a strain rate range of 1 × 10−4 to 1 × 10−3 s−1.