Abstract
Mica glass-ceramics can be applied in all kinds of electrical equipment, locomotive internal circuits in high-speed rail, ordinary electric locomotive and subway locomotive. In this study, mica glass-ceramics were prepared by sintering process using flake mica and waste glass as the main raw material with low cost. Different mica glass-ceramic samples were fabricated by changing the formula of raw materials, molding process and sintering temperature. X-ray diffraction, scanning electron microscopy, three-point bending test, and balanced-bridge technique were applied to investigate the phase, microstructure, mechanical and electrical resistivities of the samples, respectively. The results show that the optimum sintering temperature is 900 to 1000 °C holding for two hours, the desirable ratio is 70 wt% of mica powder while 30 wt% of glass powder. In that condition the sample could be less porosity, high flexural strength (63.3 MPa) and eligible electrical resistivity (0.4×1013 Ω·cm).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.