In order to clarify relationship between plasticity and microstructure for a Ni 60Pd 20P 17B 3 bulk metallic glass (BMG) at cryogenic temperature, we investigated the microstructures of both the shear band and fracture surface for the BMG compressively fractured at room temperature (RT) and 77 K (liquid Nitrogen temperature) using transmission electron microscopy (TEM). HRTEM images from the BMG fractured at 77 K clearly reveal that there are nanocrystalline particles around both shear band and fracture surface, but not in undeformed region. The sizes of the particles fractured at 77 K are smaller than those fractured at RT. These particles ranged from 3 to 5 nm in size are thought to consist of an fcc palladium–nickel solid solution phase. The particles with smaller size and the ductile fcc phase may effectively restrain the propagation of shear bands, resulting in enhancement of plastic deformation at cryogenic temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.