Abstract
Co-based coating has been fabricated on Ti-6Al-4V (TC4) titanium alloy by laser cladding. The phase composition and microstructure of the coating were analyzed using metallurgical microscope (MM), scanning electron microscope (SEM), x-ray diffraction (XRD), energy-dispersive spectroscopy (EDS) and transmission electron microscopy (TEM), respectively. The microhardness, high temperature wear resistance and corrosion resistance of the coating were investigated by performance tests. The results show that the coating was mainly composed of CoTi, CoTi2 and Co0.5Cr1.5Ti crystalline phases and an amorphous phase. The microhardness of the coating was twice that of the titanium alloy substrate. The value of friction and wear coefficient of the coating was lower and more stable, and the wear mass loss decreased by 52% as compared with the substrate in the high-temperature friction and wear test. The oxidative wear mechanism in the condition of high temperature friction and wear was studied. Moreover, the coating exhibited better corrosion resistance than the substrate in both NaCl and H2SO4 electrolyte solutions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.