Abstract
Novel reactive technique has been employed in synthesis of 7075 Al matrix composites, and effect of TiB2 particles on sedimentation and microstructure of 7075 Al Alloy in near liquidus was investigated. Researchers have shown that 4.5%TiB2/7075 composites had the smallest grains and the minimum liquidus and solidus temperatures in 7075 Al matrix composites. 4.5%TiB2/7075 composites holding for 21 hours appeared stratification phenomenon, the globular grains were 61μm and 214μm, 250μm and 283μm with the increase of holding time respectively. The microstructures evolution of TiB2 /7075 composites holding for different time at 635°C was a two-stage mechanism that the globular grains was formed firstly and secondly sedimentation and layering were began after a period of time of Ostwald ripening. The globular grain continued to increase during the settling process.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.