Abstract

ABSTRACTThe microstructure evolution of semi-solid SiCp/AZ91D nanocomposite during isothermal heat treatment process in the mushy-zone was investigated. The results indicate that the nano-size SiC particles in composite are distributed uniformly and the grains are refined significantly by the addition of nano-size SiC particles. The semi-solid microstructure evolution experiences four stages during isothermal heat treatment process: the initial coarsening, structural separation, spheroidization and final coarsening. The grain size of the primary α-Mg phase decreases with the increasing of holding temperature. With the prolongation of holding time, the grain size of the primary α-Mg phase decreases at first and then increases. The optimum isothermal heat treatment parameter is 575℃ for 30min, under which the average grain diameter is 58μm and shape factor is 1.25.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.