Abstract
Abstract In this paper, billets of Al-1080 were successfully processed by ECAP up to 1 pass, and a combination of ECAP + extrusion with extrusion ratios of 2 and 8 through a newly designed integrated die at room temperature. The combination of ECAP + extrusion processes was observed to produce finer grain sizes with greater fractions of high angle grain boundaries (HAGBs) than the ECAP. The average grain size was further decreased and the fraction of high angle grain boundaries (HAGBs) was increased with the increase of the extrusion ratio. Direct extrusion after ECAP enhanced the mechanical properties (tensile strength and hardness) with conserving reasonable degree of ductility (elongation %). ECAP and ECAP + extrusion processed samples, showed large dimple size in the tensile fracture surfaces with clear ductile fracture mode.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.