Abstract
This paper demonstrates the production of 〈00l〉-oriented CuO-doped (K0.476Na0.524)NbO3 (KNN) piezoelectric ceramics with a polymorphic phase transition (PPT) temperature greater than 180 °C by templated grain growth (TGG) using high aspect ratio NaNbO3 template particles. A novel (to the KNN system) two-step sintering and annealing process combined with CuO doping is demonstrated to improve density and maximize texture quality (F00l = 99% and rocking curve FWHM = 6.9°) in textured KNN ceramics. The best electromechanical properties (kp ≈ 0.58, k31 ≈ 0.33, d33 ≈ 146 pC/N, To-t ≈ 183 °C, Tc ≈ 415 °C, εr = 202, and tan δ = 0.016) are achieved in 1 mol% CuO-doped KNN with F00l = 99% and a relative density of 96.3%. The values of d33, kp, and k31 are 70–90% higher than randomly oriented ceramics and are obtained without a significant reduction in the PPT temperature, resulting in stable piezoelectric performance over a wide temperature range (−50 to 180 °C). These results show that high-quality textured KNN can be obtained by TGG and that a reactive matrix is unnecessary.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.