Abstract
Hard nano-structured metal matrix composite (MMC) boride coatings have been synthesized by laser melting of pre-placed powder mixture paste of B 4C + sol–gel derived nano-particulate TiO 2 on AISI 1050 (EN43) medium carbon steel and AISI 316L stainless steel substrates. Different coating/processing gas conditions were employed to understand the influence of graphite and nitrogen gas interactions with the coating material at high temperatures. Laser synthesized coatings were characterized by SEM, EDX, FEGSEM, XRD and HRTEM. Results show that it is possible to synthesize nano-structured MMC coatings (with TiB 2 and TiB particulates in the ranges of 5–10 nm, 20 nm and 200–500 nm) by employing the combined laser and sol–gel route. Nano-particulate and sub-micron level TiB and TiB 2 are found dispersed throughout the metal matrix. Other borides and carbides are present in micro-level patches dispersed in a eutectic matrix. Hardness of the composite coatings is in the range 800–2000 HV 0.1. The minimum coefficient of sliding friction obtained in a pin-on-disc set-up was 0.35 (against cemented tungsten carbide) while wear rates (against diamond) were substantially improved (up to 5 fold reduction) over that of the substrates.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.