Abstract
In this paper, AZ31B magnesium alloy/LY12 aluminum alloy were bonded together with copper foil as interlayer by vaeuum diffusion bonding technology at different temperature for holding time 60 min and pressure 2.5MPa. Analysis the microstructure of the joint under the condition of 450°C,and the effects of heating temperature on the shear thrength , microhardness and the width of the interface zone were studied. The results showed that under the condition of 450°C in holding time 60 min and pressure 2.5MPa, the microstructure at interface zone of diffusion brazing joint includes α-Mg solid solution, Mg2Cu, Cu2Mg, γ-Cu solid solution, CuAl, CuAl2 and β-Al solid solution. The width of the interface increases with brazing temperature increasing, and the microhardness gradient of interface zone in the side of aluminum alloy is much higher than that in magnesium alloy side. As the welding temperature increases, the shear strength shows an increasing trend at first and then decreases. When the welding process is 460°C keeping for 60 min, welding pressure is 2.5Mpa, the highest shearing strength of the joint can reach 35 MPa.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.