Abstract
The influence of Lu2O3 on phase transformation and seeds morphology was investigated. The result showed that the β-Si3N4 seeds with up to 95% β phase content could be obtained with 2wt% Lu2O3 as the additive content under 1750°C for two hours. The microstructure and mechanical properties of hot-pressed Si3N4 ceramics, using 9wt.% of Lu2O3• additives were investigated by the means of MTS measurements and Vickers indentation crack size measurements, as well as XRD and SEM. It was known that the high fracture toughness of Si3N4 ceramics was attributed to the rodlike morphology of β-Si3N4 grains. And the reinforcement effect and mechanism of β-Si3N4 seed were studied. It was found that the grain size and its distribution influence the property and microstructure of Si3N4 ceramics, namely, the relative narrow distribution of grain diameter in some extent and relative wide range of bimodal distribution of grain aspect ratio could improve the property of Si3N4 ceramics. The improvement in the fracture toughness with the amount of additive was mainly attributed to elongated grain growth during the sintering process.The high temperature properties of self-reinforced Si3N4 with different additives were studied. By this method, self-reinforced Si3N4 ceramics with an increment of 10~20 percent of fracture toughness was successfully fabricated.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.