Abstract
Ceramic composites in the system ZrB 2–(15–20 vol% MoSi 2) were produced by different densification techniques: pressureless sintering, hot-pressing and spark plasma sintering. Regardless of the sintering technique, the addition of 15–20 vol% MoSi 2 was beneficial for the densification of these composites. Nearly fully dense materials (98–99%) were obtained at 1750–1800 °C by the pressure-assisted techniques and at 1850 °C by pressureless sintering. All the microstructures were very fine, with mean ZrB 2 grain sizes between 1.4 and 2.5 μm. Vickers hardness, fracture toughness, Young's modulus and CTEs were similar for all the materials produced. The room temperature flexural strength varied between 500 and 700 MPa. At 1200 and 1500 °C, the highest values of flexural strength were obtained for the pressureless sintered material (655 and 500 MPa, respectively). The high-temperature flexural strength of the hot-pressed and spark plasma sintered samples was negatively affected by residual silica pockets.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.