Abstract
Abstract The microstructure and mechanical properties of the rheoformed parts of 7075 aluminum matrix composite were investigated. The results show that more liquid phase and spheroidal solid grains were found in the microstructures in the top and medium regions of the side wall of the rheoformed parts due to dependence of the deformation on liquid flow and flow of liquid incorporating solid grains. Yield strength and ultimate tensile strength of the rheoformed composite parts are enhanced as compared with the as-extruded and the rheoformed parts of 7075 matrix alloy. The yield strength, ultimate tensile strength and elongation of the rheoformed composite parts with T6 reach 399 MPa, 492 MPa and 9.6%, respectively. When stirring time increases from 5 min to 20 min, the mechanical properties increased due to fine-grained strengthening and a further increase more than 20 min led to a slight change. Pressure led to a significant increase of the mechanical properties due to some reduction of defects and dislocations strengthening. An increase of SiC volume fraction from 0.5% to 1% led to an improvement of yield strength and ultimate tensile strength and a further increase led to a decrease.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.