Abstract
The microstructure and mechanical properties of resistance-spot-welded A5052 aluminum alloy and DP 600 dual-phase steel joint were studied. The fusion zone (FZ) and heat-affected zone (HAZ) of DP 600 exhibited lath martensite and ferrite-martensite structures, respectively. The microstructure of FZ and HAZ in the A5052 side was composed of cellular crystals and the boundary region of FZ exhibited a columnar crystal morphology. A Fe2Al5 intermetallic compound (IMC) layer with 3.3μm thickness was found adjacent to the DP 600 side, whereas a needle-shaped Fe4Al13 IMC layer with length of 0.67μm to 15.8μm was found adjacent to the aluminum alloy side. The maximum tensile shear load of the A5052/DP 600 joint was 5.5KN, with a corresponding molten nugget diameter of 6.3mm. The fracture morphology of the optimized A5052/DP 600 joint was mainly an elongated dimple fracture accompanied by cleavage fracture.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call