Abstract
Ternary Bi-31.5Sn-25.0In solder has been proposed and studied for application in temperature-sensitive electronic components. In a Bi-31.5Sn- 25.0In solder joint, In was detected in an intermetallic compound (IMC) layer formed at the solder/Cu substrate interface with a thickness of 4.8 μm. The microstructure of the bulk solder consisted of Sn-rich phases distributed in Bi-rich phases with dispersion of In in both phases. Meanwhile, the nanomechanical properties of the Bi-31.5Sn-25.0In solder showed great strain rate sensitivity. To be specific, hardness increased from 9.91 MPa to 56.84 MPa as the strain rate increased in the range of (0.0005-0.125) s−1. The strain-rate sensitivity exponent (m) was found to be 0.28, indicating that the excellent ductility was shown for the solder tested under the present conditions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.